Universal Yacht Primer 1k

A multifunctional single-component marine primer based on chlorinated rubber, recommended for use on laminate, wood, and steel.

It is certainly the easiest-to-use primer from the Sea-Line brand.

CapacityCode
750 ml 300008172
2,5 l 300008174
Universal Yacht Primer 1k

Technical informations

Color

  • grey (matt)

Product description "Universal Yacht Primer 1k"

  • 1-component chlorinated rubber primer
  • Recommended above and under the water line
  • It can be use on GRP, steel and wood (except TEAK)
  • After coating with epoxy primer also applicable on aluminium
  • Does not require sanding between coats
  • Provides a transition layer between different systems and increases adhesion between the layers
  • Could be used as a sealer or barrier coat on antifoulings
  • Anti-corrosion properties in layer 390 µm
  • Good flow gives a perfect finish

Basic information

TypeGRP- laminates, wood, stel
PlaceAbove and below waterline
FunctionGrounding
Intercoating
Applicationbrush, roll, spray gun
ThinningThinner for 1 – component primer, varnisch, enamel
Theoretical coverage For 1l~7 m2 for 140 μm WFT/ 65 μm DFT
Number of coats1 – 5
Dust dry 20°C1 h
Resistant against rain 20°C4 h
Waterproof 20°C16 h
Time to launch 20°Cmin. 24 h
Elapsed time before applying next coat 20°Cmin. 5 h

You have questions about the product - Universal Yacht Primer 1k

    Also check

    Our FAQ answers to frequently asked questions

    Is it necessary to always sand the surface between application of two different products?

    We recommend to always sand the surface between applying two different products to ensure uniform surface roughness and adhesion of subsequent layers. The sanded surface should also be cleaned and degreased.

    Why the resin does not harden?

    Possible causes

    • Too low temperature of ambitne,
    • Incorrect proportion of base and herdener,
    • Mixing two components from two different manufacturers

    How to prevent

    • Apply the correct proportions of components
    • Maintain steady temperature (around 20ﹾC) during whole hardening process,
    • Mix the products thoroughly and bleed the mixture.

    How to remove

    • The uncured mass requires complete removal from the surface.

    Why the epoxy filler does not harden?

    Possible causes

    • Incorrect proportion of base and herdener,
    • Too low temperature of ambient and surface (less than 10ﹾC),
    • Mixing two components from two different manufacturers,

    How to prevent

    • Apply the correct proportions of components
    • Maintain steady temperature (around 20ﹾC) during the whole hardening process,
    • Use base and hardener from the same manufacturer

    How to remove

    • The uncured mass requires complete removal from the surface.