Polymer

Is elastic sealant recommended for sealing and bonding various types of materials.

PRODUCT DESCRIPTION:

POLYMER is recomended for use on :




Characteristic features of POLYMER

BASIC INFORMATION:

MS POLYMER

Type laminat, steel, wood, concret, plexi, etc.
PlaceAbove and below waterline
Functionsealing

bonding

Chemical characterhybrid
Densinity1,44 g/cm³
Curing mechanizmapsorption of moisture from air
Elogation at breakto 500% (DIN 53 504)
Tensile strenght3,0 N/mm² (DIN 53 504)
Tear resistance20 N/mm
Resistant to temperatures-40ºC to + 90ºC
Resistant to temperatures for short intervalsto +120ºC (white, black)
to +100ºC (transparent)
Time for skin formation 20ºC15 minut
Curing time 20ºC24 h (weld to 3 mm)
Time to contact with water 20ºCmin. 30 minutes
Time to be painted 20ºC3 day
Shrinkno

COLOR / PACKAGING / CODE

WHITE 200 ml  /  code : 8208

BLACK 200 ml  /  code : 8210

TRANSPARENT 200 ml  /  code : 8211

 

SURFACE PREPARATION:

Apply on surfaces no need to priming.

Steel surfaces is recommend to prime using Epoxy Anticorrosion primer 4:1 Sea-Line.

Wood and concrete is recommend to prime using Epoxy Woodprimer 10:4 Sea-Line.
In case of application on natural wood, its humidity should be lower than 20%.

Clean surfaces from rust, damage paint coatings, etc. To increase adhesion, is recommend to sand surfaces by sand paper :

Clean surfaces from dust and contamination.

Grease and salt remove using Cleaner Sea-Line®

APPLICATION:

Thanks to advance dispensing system, POLYMER does not require extra tools to application,  provides exact thickness of weld during application.


MS POLYMER 1

unlock nozzle


MS POLYMER 2

unlock dosing regulator


MS POLYMER 3

set dosing regulator accordance with the needs


MS POLYMER 4

apply product by pressing lever


MS POLYMER 5

after finishing  application, secure dosing nozzle and block dosing regulator


Technical information:


Share:

Do you have any questions?
We will respond as soon as possible

Related products

from Polymer


See also
Other products in this category

Our FAQ
Answers to frequently asked questions

Why the epoxy filler does not harden?

Possible causes

  • Incorrect proportion of base and herdener,
  • Too low temperature of ambient and surface (less than 10ﹾC),
  • Mixing two components from two different manufacturers,

How to prevent

  • Apply the correct proportions of components
  • Maintain steady temperature (around 20ﹾC) during the whole hardening process,
  • Use base and hardener from the same manufacturer

How to remove

  • The uncured mass requires complete removal from the surface.

Why does the paint have no adhesion?

Possible causes

  • Wrong surface preparation,
  • Skipping the primer in the system application process,
  • Use of universal thinners or replacements ,
  • Paint incompatibility.

How to prevent

  • Correct surface preparation (grinding, clearing, degreasing),
  • Use primers which improve adhesion of paints,
  • Use thinners which are dedicated to each paints,
  • Use of paints which are compatible to each other.

How to remove

  • Grind, clean and paint again.

Can I paint a boat, previously painted with 1 component paint, with polyurethane?

It is not recommended to apply 2K paints over 1K paints. 1K and 2K inks differ in their composition and properties, including hardness, chemical resistance and durability. 1K paints are one-component and dry by evaporating the solvent, while 2K paints are two-component and need to be cured by adding a hardener. Applying 2K paint over 1K paint can cause unpredictable chemical reactions and lead to undesirable effects such as dulling, chipping or flaking of the paint. Therefore, always use paints according to the manufacturer’s instructions and do not mix different types of paints. farby zgodnie z instrukcjami producenta i nie mieszać różnych rodzajów farb.