Primarily designed for the companies which produce goods or forms made of gelcoat or an industrial topcoat with a high toughness degree.

DOES NOT CONTAINS SILICONS OR FILLERS


PRODUCT DESCRIPTION:

S08 Industrial Force Sea-Line removes grinding scratches from gelcoat surface after treatment with sandpaper of gradation P600 or higher.

Using S08 Industrial Force compound allows for shortening the labour time thanks to a high cutting force.

Specialistic polishing paste with a very high cutting force which guarantee quick removal of defects and grinding scratches from a different kind of gelcoat (especially for polishing of industrial gelcoat)

BASIC INFORMATION:

CATEGORY:

SURFACES:

POLISHING:

PACKAGING:

COLOUR:

ADVANTAGES:

Surfaceswhite gelcoat
gelcoat finished products
tool gelcoat
industrial varnishes
Categoryproduction
Functionremoving defects from the surface
Consistencypaste
Surface preparation *mechanical grindingmanual grinding
light colordark colorlight colordark color
gelcoatP600⇒P800⇒P800⇒P1200⇒
tool gelcoat (technical)P800⇒P1200⇒P2000⇒
high hardness surfacesP800⇒P1200⇒P2000⇒

*grinding paper minimal gradation

Method of use:

Surface preparation :

Clean surface destined for polishing.

P600Polish surface with sandpaper of final gradation : minimum P600 →


szlifowanie papierem P800Dark colours or hard surfaces polish with sandpaper of final gradation : minimum P800 →.


Use applicators:

More applicators Sea-Line® / BRAYT

Wool applicators Sea-Line® :

wełna-dwustronna-2Double-sided wool Sea-Line:

(code : 300006614)


wełna-jednostronnaOne side wool Sea-line :

(code: 300006613)


Sponge applicators BRAYT:

gąbka-białaPolishing sponge “PROFI” :

(code :300005933)


gabka-polerska-na-rzep-grubaPolishing sponge whit velcro :

(white – code : 300000384)


Special applicators Sea-Line® :

wełna-pol.-kula-2Polishing wool BALL (80mm) Sea-Line :

(Kod : 300006619)


Polishing :

Clean surface, apply compound onto an element or head (wool or tough sponge)


praca rotacyjna Apply compound at minimum rotations on the whole surface that is being polished (800-1000 rotations/min) polishing until it changes colour and compound changes its texture


max obrotySlowly increase speed max. to 1800 RPM working with a little pressure


Further steps :

Clean surface. If after using S08 left any defects:


In order to protect surface, it is recommended to use:

TECHNICAL INFORMATION:


Μετοχή:

Έχετε ερωτήσεις;
Θα απαντήσουμε το συντομότερο δυνατό

Σχετικά προϊόντα

από S08 INDUSTRIAL FORCE CUT – στίλβωση πάστα


Δείτε επίσης
Άλλα προϊόντα αυτής της κατηγορίας

Οι συχνές ερωτήσεις μας
Απαντήσεις σε συνήθεις ερωτήσεις

Why despite the use of antifouing paint the bottom of the boat is overgrown?

Possible causes

  • Too thin layer of antifouling paint,
  • Choosing the wrong antifouling to type of a boat or yacht
  • Thinning of antifouling paint,
  • Incorrect surface preparation before antifouling application.

How to prevent

  • Apply the right layer thickness of paint indicated by manufacturer,
  • Choose antifouling dedicated to type of boat or yacht and suitable for the type of water,
  • Do not thin antifouling because of the risk of reducing effectiveness,
  • Careful surface preparations (grinding, clearing, degreasing),

How to remove

  • Wet grinding, apply new layers of antifouling paint.
  • Use C1 shell and fouling remover.

Contamination in topcoat paint?

Possible causes

  • Inaccurate surface cleaning before paint application,
  • Incorrect painting tools preparation (brush and roll),
  • Performing work in a place exposed to constant contact with dust.

How to prevent

  • Careful surface preparation (grinding, clearing, degreasing),
  • Careful painting tools preparation before use,
  • Maintain clean work environment

How to remove

  • Grind, clean and paint again.

Why the resin does not harden?

Possible causes

  • Too low temperature of ambitne,
  • Incorrect proportion of base and herdener,
  • Mixing two components from two different manufacturers

How to prevent

  • Apply the correct proportions of components
  • Maintain steady temperature (around 20ﹾC) during whole hardening process,
  • Mix the products thoroughly and bleed the mixture.

How to remove

  • The uncured mass requires complete removal from the surface.